Nickel YSZ Anode Ink (NiYSZ)

Nickel YSZ Composite Anode Ink offers good adhesion to the dense electrolyte surface which can enhance your overall cell performance. This ink is made using a high-quality ink manufacturing processes that provide a screen printable ink for easy incorporation into your own cell manufacturing process.

• Formulation: 66% by weight NiO and 34% by weight (Y₂O₃)_0.08(ZrO_2)0.92
• Solids Loading: 73 - 77% by weight

• This is a great ink for making anode catalyst layers for SOFC applications.
• Stirring the ink before use is highly recommended. For best results, the ink should be stirred with a spatula or a glass rod to achieve an even consistency prior to use.
• In order to establish a catalyst layer that is well-bonded to the electrolyte, anode ink applied electrolytes need to be sintered at 1300 °C for 1 hr (after the ink is gradually dried at 100 °C for 1 hr and then at 800 °C for 1 hr).  
• If the intend is to make electrical connections to a current collector (mesh or wire), then the ink needs to be dried at 100 °C for 1 hr and then at 800 °C for 1 hr to have good bonding with the current collector mesh or wire.
• This ink can be used for screen printing for generating electrical connections for wire attachments.

Ensuring a solid connection between your electrodes and current collector is critical for obtaining good test results. Leveraging our experience in electrochemical testing, testing we have we offer the following suggestions for obtaining optimum results with our silver paste product.